PREPARATION:

Grind to given Length of Joint ( 20 mm for KHST-5 & 25 mm for KHST-80) with grinding machine.

Clean & adjust the part of joint Knife to remove the loose particles of Rubber etc.

Apply a thin coat of Adhesive to skived area of both ends and allow it to dry until slightly sticky.

position both ends correctly in pre-heated ( at 70ºc ) Press.

Leave Joint in press for a minimum of 3 minutes in case of SR-5 & 10 minutes in case of ST-80 under heat & Pressure.

Switch off power & allow the joint to cool under pressure.

Tension must not be applied before Joint is completely cool.

TECHNICAL PARAMETERS

	KHST-5	KHST-51	KHST-80
Thickness	0.55mm	0.60	0.80mm
Breaking Strength	75Kg/Cm	8.5kg	95kg/Cm.
Elongation at Break	20%	18%	18%
Surface Cylinder Side	Elastomer coated Polyamide Fabric	18%	Elastomer Coated Polyamide Fabric
Wharves Side	Blend of Cotton & Polyamide Fabric	18%	Blend of Cotton & Polyamide Fabric
Coefficient of Friction Cylinder Side	0.55	18%	0.55
Wharves Side	0.28		0.28

UNMATCHED CHARACTERISTICS		UNBEATABLE RESULTS
Light Weight & High Flexibility. High Strength & High Elasticity. High Coefficient of Friction on drum side High Abrasion Resistance Permanently Antistatic Quick Splicing and Jointing.		Saving in Power Consumption up to 14 % uniform Spindle Speed & Excellent yarn Quality. Low idle spindlage - Higher productivity Quick acceleration to required speed. Braking a spindle does not affect adjacent spindles No accumulation of fluff, Minimum downtime of machine.